The mean SBS values of all composit

The mean SBS values of all composites tested were
greater than the 5.9 MPa, considered by Reynolds20 to be
adequate for routine clinical use. However, for the flowable
composites, the 30–40% failure rate was clinically unacceptable
(Table 2). The maximum bond strength recommended
for successful clinical bonding is estimated to be
7 MPa.21 In another study, shear stresses exerted on attachments
during orthodontic treatment were reported to range
from 1 to 3 MPa,22 although higher stresses can occur during
mastication.23 Studies have shown that metal brackets
bonded with composite resins show bond strengths ranging
from 2 to 13 MPa

Hasil (Bahasa Indonesia) 2:

Nilai-nilai SBS mean dari semua komposit yang diuji
lebih besar dari 5,9 MPa, dianggap oleh Reynolds20 menjadi
cukup untuk penggunaan klinis rutin. Namun, untuk mengalir
komposit, tingkat kegagalan 30-40% secara klinis tidak dapat diterima
(Tabel 2). Kekuatan ikatan maksimum yang dianjurkan
untuk ikatan klinis sukses diperkirakan
7 MPa.21 Dalam studi lain, tegangan geser diberikan pada lampiran
selama perawatan ortodontik dilaporkan berkisar
dari 1 sampai 3 MPa, 22 meskipun tekanan yang lebih tinggi dapat terjadi selama
Studi mastication.23 telah menunjukkan bahwa kurung logam
terikat dengan resin komposit menunjukkan kekuatan ikatan mulai
2-13 MPa